Published May 2024, Pg. 32-36

Section: Oil field equipment

UOT: 621.242.6

DOI: 10.37474/0365-8554/2024-05-32-36

Graphoanalytical method for determining plasticity properties for structural materials

S.A. Musavi PhD in Tech. Sc. - Azerbaijan State Oil and Industry University

The presented article sets the task of assessing and determining the plasticity of materials for the manufacture of elements of SOFC structures, manufactured on the basis of bodies in a complex stress state. To obtain estimated values of the plasticity of materials, a linear call of hardening of a deformable body is considered. As a result of the hypothesis about the strengthening of materials due to the reduction of pores, it was established that the plasticity coefficient of elastic-plastic bodies depends on its elastic parameters, porosity and deformation angles and does not depend on the factor of brittle fracture under load.
A graphic-analytical method has been proposed for determining the plasticity coefficient of materials and therefore it uses all parameters explicitly to evaluate the properties of all groups of materials, including materials for SOFC.

References:

1. B.N. Arzamasov i dr. Materialovedeniye: Ucebnik dlya vuzov 3-е izd.,– М.: İzd-vo MQТU im. N.E. Baumana, 2002, 648 s.

2. Valiyev Р.Z., Aleksandrov I.V. Nanostrukturnye materialy, polucenye intensivnoy plasticeskoy deformatsiyey. – M.: Logos, 2000, 272 s.

3. Qutkin М.Y., Оvid′ko I.А. Defekty i mexanizmy plasticnosti v nanostrukturnykh i metallicheskikh materialax. – SPb.: Logos, 2001, 178 s.

4. Milligan W.W., Hackney S.A., Ke M., Aifantis E.C. In situ studies of deformation and fracture in nanophase materials. pp. 267-276: 

5. Robert J. Asaro, Subra Suresh. Mechanistic models for the activation volume and rate sensitivity in metals with nanocrystalline grains and nano-scale twins. Acta Mater 53 (2005) 3369-3382.

6. Feichtinger D., Derlet P.M. and Swygenhoven H.V. Switzerland ~Received 7 Paul Scherrer Institute, 5232 Villigen, November 2002; published 23 January 2003

7. Van Swygenhoven S.H., Derlet P.M., Budrovic Z., Hasnaoui A. Unconventional deformation mechanism in nanocrystalline metal Switzerland Acta Mater. Paul Scherrer Institute, CH-5232 Villigen, 50 (2002) 3957.

8. Schiotz, J. Jacobsen. A maximum in the strength of nanocrystalline copper. Science. 301 (5638), 1357-1359 (2003). Conrad

9. Hasnaoui A., Van Swygenhoven H., Derlet P.M.  Science 296, April 4, PRB 64, 224105. Acta mater 51 (19), 5743-5774.